Ti-6Al-2Sn-4Zr-6Mo titanium alloy
Ti6-2-4-6 is a heat treated alpha-beta titanium alloy for which you can get higher properties than TA6V. Its strengths are a better resistance, a low cycle fatigue and a good ductility. It can resist to tempratures up to 450°C. This metal is mainly used for turbines, discs or blades.
Key benefits
-
Low elasticity modulus
-
Low density/weight ratio
-
Fatigue resistance
Chemical composition
Reference standard : AMS 4981
Al
- 5,5% min
C
- 0% min
Sn
- 1,75% min
N
- 0% min
Zr
- 3,5% min
H
- 0% min
Mo
- 5,5% min
Cu
- 0% min
Fe
- 0% min
O
- 0% min
Ti
- —
Back
Mechanical properties
Rm (Mpa)
1034
Rp 0,2 (Mpa)
965
Density (g/cm3)
4,64
A (%)
6
Z%
15