Stainless steel
316 L (ESR/VAR)
1.4441
Cold worked stainless-steel
316 L (1.4441) is an austenitic stainless steel whose basic composition is similar to the 316L (1.4435), except with a much stricter tolerance to impurities. This gives the steel a better resistance to corrosion than ordinary 316L, making it more suitable for medical applications (and especially implants).
Key benefits
-
Excellent corrosion resistance
-
Biocompatibility
-
For implants and instruments
Standards
ASTM F138
ASTM F139
ISO 5832-1
Formes disponibles
Diameter
- 5 to 19 mm
Length
- 3000 mm approx.
En stock
Granulometry
- Any kind of granulometry suitable to your machine
En stock
Thickness
- 1 mm to 6 mm
Dimensions
- 300 mm to 320 mm (foils)
- 1000 mm (sheets and plates)
Sur demande
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Sur demande
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Sur demande
Chemical composition
Reference standard : ASTM F138
C
- 0% min
Si
- 0% min
Mn
- 0% min
P
- 0% min
S
- 0% min
Cr
- 17% min
Mo
- 2,25% min
Ni
- 13% min
Cu
- 0% min
N
- 0% min
Fe
- —
Back
Mechanical properties
Rm (Mpa)
860 ≤ Rm ≤ 1100
Rp 0,2 (Mpa)
690
Density (g/cm3)
7.9
A (%)
12