Cobalt chrome
MP35N
This non-magnetic nickel, cobalt, chromium and molybdenum based alloy offers a unique combination of high tensile strength (up to 2068 Mpa), good ductility and excellent corrosion resistance. Besides, it shows an exceptional resistance to sulfuration, oxidisation at high temperature and weakening by hydrogen.
Key benefits
-
Corrosion resistance
Standards
ASTM F562
ISO 5832-6
Formes disponibles
Diameter
- On demand
Length
- On demand
Sur demande
Chemical composition
Reference standard : ASTM F562
C
- 0% min
Cr
- 19% min
Mo
- 9% min
Ni
- 33% min
Fe
- 0% min
Si
- 0% min
Mn
- 0% min
P
- 0% min
S
- 0% min
Ti
- 0% min
Bo
- 0% min
Co
- —
Back
Mechanical properties
Rm (Mpa)
800 (annealed)
Rp 0,2 (Mpa)
300 (annealed)
Density (g/cm3)
8.43
A (%)
40 (annealed)